陶氏高密度聚乙烯 DMDA-8904 NT 7
High Density Polyethylene Resin
陶氏塑料
Technical Data
产品说明
• Injection molding
• For injection molded pails, industrial parts and other shipping containers
• Excellent impact strength, stress crack resistance and processability
• Very narrow molecular weight distribution
Complies with:
• U.S. FDA 21 CFR 177.1520 (c)3.1a
• Canadian HPFB No Objection
• EU, No 10/2011
Consult the regulations for complete details.
DOW DMDA-8904 NT 7 High Density Polyethylene (HDPE) Resin is produced via UNIPOL™ Process Technology from Dow and is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. This resin has been designed to provide excellent processability for molders and to meet the rigorous performance characteristics of applications requiring stackability, environmental stress crack resistance and impact strength. This resin is also suitable for cast film extrusion processing.
总体
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet
UL 黄卡 2 • E337483-100635873
搜索 UL 黄卡 • 陶氏塑料
供货地区 • 北美洲 • 拉丁美洲 • 亚太地区
机构评级 • FDA 21 CFR 177.1520(c) 3.1a • HPFB (加拿大) No Objection • 欧洲 No 10/2011
形式 • 粒子
加工方法 • 流延薄膜 • 注射成型
物理性能 额定值(英制) 额定值(公制) 测试方法
比重 0.954 0.952g/cm³ ASTM D792
熔流率(熔体流动速率) (190°C/2.16 kg) 4.4g/10 min 4.4g/10 min ASTM D1238
抗环境应力开裂 4 (122°F (50°C), 100% Igepal, 22.0hr 22.0hr ASTM D1693
F50)
机械性能 额定值(英制) 额定值(公制) 测试方法
抗张强度 4 ASTM D638
屈服 3900psi 26.9MPa
断裂 4500psi 31.0MPa
伸长率 4 ASTM D638
屈服 9.0% 9.0%
断裂 1200% 1200%
弯曲模量 - 2% 正割 4 160000psi 1100MPa ASTM D790B
薄膜 额定值(英制) 额定值(公制) 测试方法
薄膜厚度 - 经测试 1.0mil 25µm
膜耐刺穿性 (1.0 mil (25 µm)) 8.00ft•lb/in³ 0.662J/cm³ 内部方法
割线模量 ASTM D882
2% 正割, MD : 1.0 mil (25 µm), 铸造薄膜 81300psi 560MPa
2% 正割, TD : 1.0 mil (25 µm), 铸造薄膜 91700psi 632MPa
抗张强度 ASTM D882
MD : 屈服, 1.0 mil (25 µm), 挤塑薄膜 3510psi 24.2MPa
TD : 屈服, 1.0 mil (25 µm), 挤塑薄膜 3010psi 20.7MPa
MD : 断裂, 1.0 mil (25 µm), 挤塑薄膜 6630psi 45.7MPa
TD : 断裂, 1.0 mil (25 µm), 挤塑薄膜 5640psi 38.9MPa
伸长率 ASTM D882
MD : 断裂, 1.0 mil (25 µm), 挤塑薄膜 690% 690%
TD : 断裂, 1.0 mil (25 µm), 挤塑薄膜 940% 940%
陶氏高密度聚乙烯 DMDA-8904 NT 7
High Density Polyethylene Resin
陶氏塑料
薄膜 额定值(英制) 额定值(公制) 测试方法
落锤冲击 (1.0 mil (25 µm), 铸造薄膜) 28g 28g ASTM D1709A
埃尔曼多夫抗撕强度 ASTM D1922
MD : 1.0 mil (25 µm), 铸造薄膜 22g 22g
TD : 1.0 mil (25 µm), 铸造薄膜 160g 160g
冲击性能 额定值(英制) 额定值(公制) 测试方法
拉伸冲击强度 5, 4 40.0ft•lb/in² 84.1kJ/m² ASTM D1822
硬度 额定值(英制) 额定值(公制) 测试方法
肖氏硬度 4 (邵氏 D) 59 59 ASTM D2240
热性能 额定值(英制) 额定值(公制) 测试方法
载荷下热变形温度 4 (66 psi (0.45 MPa), 未退火) 162°F 72.2°C ASTM D648
脆化温度 4 < -105°F < -76.1°C ASTM D746
维卡软化温度 264°F 129°C ASTM D1525
溶融温度(DSC) 268°F 131°C 内部方法
结晶峰温度 (DSC) 246°F 119°C 内部方法
光学性能 额定值(英制) 额定值(公制) 测试方法
光泽度 (45°, 1.00 mil (25.4 µm), 铸造薄膜) 87 87 ASTM D2457
雾度 (1.00 mil (25.4 µm), 铸造薄膜) 3.0% 3.0% ASTM D1003
挤出 额定值(英制) 额定值(公制)
熔体温度 525°F 274°C
挤压说明
铸造薄膜的制造条件:
• EGAN/Davis 标准 5 层铸造生产线
• 熔体温度:525° F (261°C)
• 冷却辊(主/次)温度:70 °F (21 °C)
• 生产线速度:400 fpm(123 米/分)
• 输出:356 磅/小时
• 模具宽度:36 英寸 (914 mm)
• 模具间隙:25 密尔 (.65 mm)
• 气隙:3 英寸 (76 mm)